Bi-2223/Ag异质结的光生电压效应研究

在50 ～ 340 K不同温度下,利用紫色激光(λ=405 nm)对银/铋锶钙铜氧2223异质结界面进行辐照,观测到明显的光生电压效应,发现光生电压的极性分别在超导转变温度TC与320 K附近发生了反转,排除了激光产生的热电势是产生光生电压的原因,分析表明银/铋锶钙铜氧2223异质结界面处存在内建电场:光生电压由异质结界面处的内建电场分离光生电子-空穴对产生的.超导转变温度TC之下以及320 K以上,内建电场方向从超导体指向金属电极;超导转变温度TC与反向温度320 K之间,内建电场从金属指向超导体.     

Synthesis of Small‐Sized,Porous, and Low‐Toxic Magnetite Nanoparticles by Thin POSS Silica Coating

In this communication, we report the synthesis of small‐sized (<10 nm), water‐soluble, magnetic nanoparticles (MNPs) coated with polyhedral oligomeric silsesquioxanes (POSS), which contain either polyethylene glycol (PEG) or octa(tetramethylammonium) (OctaTMA) as functional groups. The POSS‐coated MNPs exhibit superparamagnetic behavior with saturation magnetic moments (51–53 emu g^?1) comparable to silica‐coated MNPs. They also provide good colloidal stability at different pH and salt concentrations, and low cytotoxicity to MCF‐7 human breast epithelial cells. The relaxivity data and magnetic resonance (MR) phantom images demonstrate the potential application of these MNPs in bioimaging.     

A post curing strategy toward the feasible covalent adaptable networks in polyacrylate latex films

The implementation of covalent adaptable networks (CANs) in general resin system is becoming attractive. In this work, we propose a simple post-curing strategy based on the core-shell structured acrylate latex for the achievement on both the improved general performance and the CANs characteristics in latex films. The building to the CANs was relied on the introduction of 4,4′-diaminophenyl disulfide as the curing agent, which cured the acetoacetoxy decorated shell polymer through the ketoamine reaction. The metathesis reaction of aromatic disulfides in the crosslinking segments enabled the thermally induced dynamic behavior of the network as revealed in the stress relaxation tests by comparison with other diamine crosslinking agents without the incorporation of disulfide. The synergism of the dynamic crosslinking of the shell polymer and static crosslinking in the core polymer contributed to the improved mechanical strength (15 MPa, strain% = 250%) and the suppressed water adsorption (~1% in 24 h of soaking) of the latex film, which exhibited above 90% of recovery in both strength and strain from a cut-off film damage within 1 h at 80°C. Moreover, the cured latex film could be recycled, and 75% of the mechanical performance was regained after three fragmentation-hot-pressing cycles. These, in addition with the feasible and environmental friendly characteristics, suggest a sustainable paradigm toward the smart thermosetting latex polymers.     

介绍一个与材料相关的研究型综合化学实验——壳聚糖的制备与表征

在中国科学技术大学夏季学期的研究型实验课程"化学科研基础训练"中开设"壳聚糖的制备与表征"综合实验,以龙虾壳为原料,通过除蛋白、脱盐、脱色、脱乙酰等一系列反应,制备得到目标产物壳聚糖。运用红外光谱、核磁共振仪、黏度法、滴定等对产品的结构及性能进行表征。     

GZO/Al复合背电极对非晶硅太阳能电池的影响

随着能源紧缺与环境污染问题的日益严重,太阳能的开发利用越来越受到重视,其中非晶硅薄膜太阳能电池由于其制备工艺简单、价格低廉等优点被广泛地研究.为了使非晶硅薄膜太阳能电池得到更好地利用,提高其转换效率和稳定性显得尤为重要.引入复合背电极是提高非晶硅太阳能电池性能的有效手段,其中对GZO/Al复合背电极的研究还未见报道.在该工作中,利用磁控溅射法在非晶硅电池上制备了GZO/Al复合背电极,研究了复合背电极的制备条件及其对非晶硅太阳能电池性能的影响.结果显示,当GZO层的溅射功率为90 W、Al层的溅射功率为90 W时,具有复合背电极的太阳能电池表现出较好的光电转换性能,其短路电流(ISC)、开路电压(VOC)、填充因子(FF)和电池的光电转换效率(η)分别为8.92 mA、1.55 V、54.48;和7.53;.相较于单层Al背电极的太阳能电池,其光电转换效率大幅提高了47.6;(相对效率).